PrimaSelect PEI Ultem 9085 - 1.75mm - 500g - Natural

More Views

PrimaSelect PEI Ultem 9085 - 1.75mm - 500g - Natural
Excl. Tax: $133.11 Incl. Tax: $166.39

Availability: Available to order

Only available from remote stock. Expect 2-4 days for delivery

PrimaSelect PEI Ultem 9085 - 1.75mm - 500g - Natural
Description

Details

SELECT Polyether Imide (PEI) Ultem 9085 is an amorphous, high performance thermoplastics with a glass transition temperature (Tg) of 186 °C. This material features superior mechanical performance, flame retardancy (UL 94-VO rated) and strength-to-weight ratio.

The PrimaCreator PEI Filament has unique properties because it does not come into contact with water during the production process and is directly packaged in a vacuum packaging. These properties make the PrimaCreator PEI Filament particularly suitable for usage in FDM and FFF 3D printers. The material has an excellent adhesion between layers which results in great improvement of the impact resistance, strength, durability and the printing process.

To make a successful PEI print there are a few things to keep in mind. The printer must have the performance to meet the PEI filament and it should be printed with a nozzle temperature of 355-390°C. The heat bed should be set to 120-160°C and a heated chamber is important to have. It´s also very important to make sure that the printer is placed in a room where there´s hardly any draft and temperature fluctuations.

PEEK is best printed on a PEI sheet at a printing speed of 15-30 mm/s.

Essential Data:

 Material

Polyether Imide

 Diameter  1.75mm
 Tolerance  ± 0.05 mm
 Heated build platform required  Yes, 120-160° C
 Print Temperature  350 - 380° C
 Recommended Print Speed  15-30 mm/s
 Weight Filament  500 grams

Technical data:

 Property Test method Value
 Density  ASTM D 72  1,34 g/cm3
 Tensile Modulus  ASTM D 638  3440 MPa
 Tensile Strength  ASTM D 638  84 MPa
 Impact strength  ASTM D 256  115 J/m2